Abstract
Abstract In this study, biobased silica/carbon hybrid nanoparticles (SCNPs) were synthesized using pyrolysis process and reinforced in to polymer film using 3D printing technique. These polymer films were further tested for their thermal and mechanical properties to determine the influence of silica/carbon nanoparticles on the properties of the biopolymer . The SCNPs were synthesized from agricultural waste rice husk by high temperature pressure reaction. These nanoparticles were characterized using X-ray diffraction (XRD), Raman Spectroscopy , and Transmission electron microscope (TEM) analysis and revealed the formation of highly crystalline cristobalite silica/carbon hybrid nanomaterial . X-ray photon spectroscopy (XPS) analysis showed the presence of elemental Si, C, and O in the as-synthesized SCNPs. Brunauer–Emmett–Teller (BET) surface area measurements showed the surface area of 223.029 m2 /g, for as prepared nanoparticles. The 3D printed biocomposites thin films were characterized by XRD, Differential Scanning Calorimetry (DSC), Thermo Gravimetric Analysis (TGA), Raman spectroscopy, FE-SEM and Tensile analysis. The FE-SEM analysis of the composites showed the uniform dispersion of nanoparticles in the biopolymer. TGA and Tensile tests revealed significant enhancement in thermal stability, maximum strain and strain to failure properties due to the integration of 0.5 and 1.0 wt% of silica/carbon nanoparticles (SCNPs). Also, DSC analysis showed the moderate improvement of glass transition temperature and crystallization temperature as compared to the neat polymer. This increase may be due to the increased crosslinking of polymer by incorporation of thermally stable SCNPs nanoparticles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.