Abstract
Different contents of bismuth oxide doped in 3YSZ material and the mixed powder formed. After press forming,the samples were sintered at 850°C, 900°C, 1000°C and 1100°C respectively. The electrical properties,the thermal shock resistance,the phase components and the microstructure morphology were analyzed to study the solid solution mechanism of Bi2O3-Y2O3-ZrO2 three-phase system. It was found that the Bi2O3 can effectively reduce sintering temperature as a flux. Sintered at 1000°C, t-ZrO2 can be induced into m-ZrO2 by Bi2O3 doped. With the increasing of Bi2O3 content, system shock resistance decreases. The thermal shock resistance of the 2-3mol% Bi2O3-YSZ is the best. In the different content of Bi2O3 system, 3mol% doped materials has the highest conductivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.