Abstract
An effect of Ar-irradiation on structural and nanomechanical properties of pure zirconium at room temperature was investigated. In order to simulate the radiation damage, the argon ions were implanted into the pure zirconium coupons with fluences ranging from 1 × 1015 to 1 × 1017 cm−2. Prior to irradiation, zirconium samples were chemically polished with a solution of HF/HNO3/H2O. Structural properties of the implanted layer were studied using Grazing Incidence X-Ray Diffraction (GIXRD) technique. The nanomechanical properties of the material were measured by means of nanoindentation technique. The obtained results revealed correlation between Ar-implantation fluence, hardness and structural properties (as confirmed by the modification of the diffraction peaks). Material hardening and peak shift & broadening in GIXD spectra were associated with the local increase of micro-strains, which is related to the increased density of type <c> - dislocation loops. Presented study confirms that the structural changes induced by ion irradiation are directly linked to the mechanical response of the sample.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.