Abstract
Amorphous soft magnetic materials have significant potential applications in specialist power transformers and in inductive devices. With the composition of Fe82Si8B10, 82% of the transition metals Fe and about 18% of metalloid or glass-former elements like B and Si are strongly magnetic at room temperature and offer dynamic opportunities for engineering applications. The crystallization kinetics has been studied by differential thermal analysis (DTA). The sample was annealed in a controlled way in the temperature range of 350-450°C at constant annealing time one hour. The kinetics of primary crystallization α-Fe(Si) phase and secondary crystallization Fe2B phase was studied as affected due to temperature. The sample annealed at 350oC temperature is almost unchanged which is still lower than that of primary crystallization temperature but the same condition when sample annealed at 450°C completely shows that the primary crystallization α-Fe(Si) phase has vanished and crystallization event took place to a good extent.
 Journal of Engineering Science 11(1), 2020, 107-112
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.