Abstract
Explosive welding of titanium Grade 1 to AW7075 aluminum alloy arranged in parallel setup was performed. The annealing of produced bimetals at the temperatures of 450, 500 and 550 °C for times ranging from 20 to 100 h was carried out after explosive welding. The produced bimetal was characteristic by its wavy interface typical for that bonding process. Increase in the microhardness at the interface was recorded due to work hardening. Delamination of titanium Grade 1 flyer sheet was firstly observed when annealing temperature of 500 °C for 40 h was carried out. Annealing at 550 °C also resulted in delamination of upper sheet. The intermetallic compound (IMC) layer was observed at the interface after annealing of bimetals. The higher the annealing temperature and time, the higher the thickness of continuous IMC layer. The maximum measured thickness of IMC layer averaged 13 µm. Energy dispersive x-ray spectroscopy (EDS) and x-ray diffraction (XRD) analyses revealed that the interface layer is consisted of Al18Ti2Mg3 IMC. Microhardness at the interface increased dramatically up to 439 HV0.1 after annealing of bimetal due to the presence of above-mentioned IMC.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.