Abstract
Thermal embrittlement caused by phase transformations in the temperature range of 204–538 °C limits the service temperature of duplex stainless steels. The present study investigates a set of wrought (2003, 2101, and 2205) and weld (2209-w and 2101-w) alloys in order to better understand how alloying elements affect thermal embrittlement. Samples were aged at 427 °C for up to 10,000 h. The embrittlement and thermal instability were assessed via nanoindentation, impact toughness testing, and atom probe tomography (APT). Results demonstrate that the spinodal amplitude is not an accurate predictor of mechanical degradation, and that nanoindentation within the ferrite grains served as a reasonable approximate for the embrittlement behavior. Compositionally, alloys with a lower concentration of Cr, Mo, and Ni were found to exhibit superior mechanical properties following aging.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.