Abstract
The results of experimental studies to determine the effect of alloying and heat treatment on the mechanical properties of the high-chromium cast iron are described. When alloying the melt with nickel, molybdenum and manganese, as well as during heat treatment by quenching, specific wear, tensile strength in bending of the obtained samples, their hardness and microhardness were studied. A comparative analysis of the influence of alloying elements and heat treatment methods has been performed. When alloying Ni, Mo, and Mn, cast specimens that have not undergone heat treatment have the highest specific wear. It was established that the hardened Ni alloyed samples have the greatest bending strength. It was found that cast samples that were not subjected to heat treatment have much lower hardness and microhardness. The approximate composition of chromium cast iron was determined for further studies to increase its wear resistance. The research results are used in the manufacturing process of parts for crushing and grinding equipment.
Highlights
The results of experimental studies to determine the effect of alloying and heat treatment on the mechanical properties of the high-chromium cast iron are described
It was found that cast samples that were not subjected to heat treatment have much lower hardness and microhardness
The approximate composition of chromium cast iron was determined for further studies to increase its wear resistance
Summary
The results of experimental studies to determine the effect of alloying and heat treatment on the mechanical properties of the high-chromium cast iron are described. Молибденом и марганцем, а также при термической обработке закалкой изучены удельный износ, предел прочности при изгибе полученных образцов, их твердость и микротвердость. Установлено, что наибольшую прочность при изгибе имеют закаленные образцы, легированные Ni, значительно меньшую твердость и микротвердость – литые образцы, не подвергавшиеся термической обработке.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY)
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.