Abstract
This paper studied the influence of Ag micro-alloying on the thermal stability and ageing characteristics of a deformation-processed Cu–14Fe in-situ composite prepared by thermo-mechanical processing. Heat treatment caused (i) edge recession, longitudinal splitting, cylinderization, break-up and spheroidisation of the Fe fibres in the Ag micro-alloyed Cu–14Fe in-situ composite, and (ii) recovery, recrystallisation and precipitation in the Cu matrix. Ag micro-alloying caused these processes to occur at lower temperatures. The index Z (a combination figure of merit that assesses the service performance) reached the peak value of 3.3×107MPa2·% IACS after isothermal heat treatment at 500°C for 1h, where IACS is the International Annealed Copper Standard, a measure of conductivity. The optimum combinations of tensile strength and conductivity were 1033MPa and 56.6% IACS; 931MPa and 58.9% IACS; or 851MPa and 60.6% IACS. The tensile strength and conductivity of Ag micro-alloyed Cu–14Fe in-situ composite at η=7.8 after isochronal heat treatments were higher than those of the Cu–14Fe in-situ composite at each temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.