Influence of adhesive-composite application modalities on their bonding to tooth structure and resistance of the performed restorations to failure

Abstract

Background/purposeThe longevity of bonded composite restorations could be affected by the utilized adhesive-composite application techniques. This in vitro study aimed to evaluate the influence of adhesive-composite application modalities on their bonding values to tooth structure and on the failure resistance of the performed restorations on loading. Materials and methodsResin composite studs, 2 mm in diameter and 4 mm high, were bonded in 2 groups to flattened enamel and dentin surfaces of 80 extracted premolars using pre-cured (PC) and co-cured (CC) self-etch resin adhesive. Studs in each group were built-up in 4 subgroups using either multiple increments of nano-filled composite (IF, control) or single increment of preheated nano-filled (PH), bulk-fill (BF) and sonic-activated bulk-fill composites (SF). Another 80 premolars with standard class II cavities were also restored using the same adhesive-composite application modalities. All specimens were then stressed on a universal testing machine to assess the composite-tooth shear bond strength and the resistance of the performed restorations to failure. The modes of specimens’ failure were also assessed following each test. ResultsThe PC adhesive provided higher bond strength to dentin (p < 0.05) and comparable bond strength to enamel in comparison to the CC one (p>0.05%). Both PH and BF composites showed lower bond strength to dentin in presence of PC adhesive (p < 0.05). Comparable bond strengths were noticed for PH, BF and SF composites to dentin in presence of CC adhesive (p > 0.05). PH and SF restorations presented the highest resistance to failure (p < 0.05). ConclusionBoth incrementally and bulky-inserted composites offer clinically acceptable bond strength in presence of pre-cured resin adhesive. Both Preheated and sonic-activated composite restorations offer the highest resistance to failure on loading. The preheating procedure renders regular composite material suitable for bulk-fill applications.