Influence of addition of indium and of post-annealing on structural, electrical and optical properties of gallium-doped zinc oxide thin films deposited by direct-current magnetron sputtering

Abstract

Abstract In this study, both gallium-doped zinc oxide (GZO) and indium-added gallium-doped zinc oxide (IGZO) thin films were deposited on commercial glasses by magnetron dc-sputtering in argon atmosphere. The crystal structure, electrical conductivity and optical transmission of as-deposited as well as post-annealed thin films of both GZO and IGZO were investigated for comparison. A small amount of indium introduced into GZO thin films had improved their polycrystalline structure and increased their electrical conductivity by over 29%. All obtained GZO and IGZO thin films have strong [002] crystalline direction, a characteristic orientation of ZnO thin films. Although post-annealed in air at high temperatures up to 500 °C, IGZO thin films still had very low sheet resistance of 6.6 Ω/□. Furthermore, they had very high optical transmission of over 80% in both visible and near-infrared regions.