Abstract
Intergranular corrosion is one of the most important processes affecting the behaviour of austenitic stainless steels. Factors such as steel chemical composition, the degree of prior deformation and the exposure temperature affect the degree of sensitisation. AISI 316L (0% CW) steel was annealed at 650 °C for 5, 10, 30, 100, 300 and 1000 h to analyse the influence of isothermal annealing on the precipitation of secondary phases. AISI 316L steel after 40% cold working and subsequent annealing at 650 °C for 1, 1.5, 2, 5 and 10 h was investigated. Time–temperature sensitisation (TTS) diagrams were created based on corrosion test (ASTM A 262, practice A) results. In the case of AISI 316L (0% CW), M23C6, chi and sigma phases precipitated at grain boundaries, and the Laves phase was mainly inside of the grains. In the case of AISI 316L (40% CW), sigma, chi, Laves and M23C6 were identified and precipitated mainly along the grain boundaries as well as on the shear bands within different annealing times. It was confirmed that the increase in the annealing time caused an increase in the amounts of secondary phases. Secondary phases in the equilibrium state were calculated using Thermo-Calc software.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.