Abstract
In this study, three thermally labile additives microcrystalline cellulose (MCC), nanocrystalline cellulose (NCC), and polyvinylpyrrolidone (PVP) were introduced to the P84-copolyimide (PI) solution. PI-based carbon tubular membranes were fabricated using dip-coating method, followed by sample characterizations in order to determine their structural morphologies, thermal stability and gas permeation performance. NCC was added as the membrane pore former for the hydrogen gas (H2) separation. While tests involving pure H2 and N2 permeation were carried out at room temperature, carbon membranes were carbonized at a final temperature of 800 °C, with the heating rate of 3 °C/min under the Ar flow. Excellent result of H2/N2 selectivity was obtained with value of 430.06 ± 4.16. Addition of NCC has significantly increased the number of pore channels in the membrane, hence, contributing to high gas permeance and selectivity. NCC has shown potential as a good additive for an enhanced hydrogen separation performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.