Abstract
The localized vibrational modes (LVMs) of silicon donor (SiGa) and aluminum isovalent (AlGa) impurities in molecular beam epitaxial GaAs layers grown at various temperatures are studied using the infrared absorption technique. It is found that the total integrated absorption of these impurities LVMs is decreased as the growth temperature decreases. This finding suggests a nonsubstitutional incorporation of Si and Al in GaAs layers grown at 200 °C. On the other hand, a subtitutional incorporation is obtained in GaAs layers grown at temperatures higher than 350 °C. A recovery of the SiGa LVMs in GaAs layers grown at 200 °C has not been achieved by thermal annealing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.