Abstract
The sludge from water treatment plants (WTP) is a waste from the water process. This study evaluated the effect of incorporating water treatment plant (WTP) sludge, replacing the water used in compacted soil–cement mixtures. The materials were characterized by Scanning Electron Microscopy (SEM) associated with Energy Dispersive Spectroscopy (EDS) and Atomic Absorption Spectrometry (AAS). The soil, with the addition of liquid WTP sludge, presented an apparent dry specific weight (ƴd) of 1.77 gf·cm−3, the optimum moisture value in the compaction test of 15%, and the cement contents tested were 7, 11, and 14%. The specimens were molded using a WTP sludge–cement–soil mixture under the conditions mentioned above, and the simple compression results showed values within the range of 2.5 to 9.3 MPa, as specified by the Brazilian Technical Standard (NBR) 8491/2012. The hydraulic conductivity performed on the test specimen after 28 days of curing resulted in a coefficient (k) of 7.49 × 10−9 cm·s−1, classified as little permeable. The result obtained from aluminum leaching was 0.12 mg·L−1, within the maximum limit allowed by NBR 10004/2004. Therefore, liquid WTP sludge has a significant capacity for incorporation into the compacted soil–cement mixture and the potential to manufacture ecological bricks, an alternative environmentally sustainable brick.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.