Abstract
ObjectiveTo evaluate the antimicrobial/antibiofilm and mechanical properties, and the effect on enamel demineralization of a resin-modified GIC (RMGIC) containing CHX and nano-sized sodium trimetaphosphate (TMP). MethodsRMGIC was associated with CHX (1.25 or 2.5%) and/or TMP (7 or 14%). Antimicrobial and antibiofilm activity were assessed using agar diffusion test and evaluation of biofilm metabolism, respectively. In addition, fluoride (F) and TMP releases as well as the diametral tensile (DTS) and compressive (CS) strength were determined. The percentage of mineral loss (%SH), integrated loss of subsurface hardness (ΔKHN) and enamel F concentrations were also evaluated. ResultsRMGICs containing CHX associated or not with TMP presented higher inhibition zones and effect on S. mutans biofilm. A reduction on CS was observed only for RMGIC + 2.5%CHX and on DTS for RMGIC + 2.5%CHX + 14%TMP. The highest F and TMP releases and lowest %SH and ΔKHN values were detected for RMGIC + 1.25%CHX + 14%TMP and RMGIC + 2.5%CHX + 14%TMP. Higher enamel F concentrations were observed for TMP groups. Conclusion1.25%CHX and 14%TMP increased antimicrobial/antibiofilm action and the ability to prevent enamel demineralization, with minimal effect on the mechanical properties of RMGIC. Clinical significanceRMGIC containing CHX and TMP is an alternative material for patients at high risk for dental caries and can be indicated for low-stress regions or provisional restorations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.