Abstract
In this research, a composite coating with Al2O3 and ZrO2 particles have been applied on AZ31 magnesium alloy by micro-arc oxidation (MAO) technique. The alkaline electrolyte included a constant based composition and different composition of the Al2O3 and ZrO2 additives. Microstructure observations reveal that the surface pores of composite coating reduced during addition of ZrO2 and Al2O3 ceramic particles. The hardness of coating increased from about 380 for non-added to 620 MPa for Al2O3+ZrO2 added coating and wear rate reduced about 8 times. Wettability of the coating increased by incorporation of Al2O3 and/or ZrO2 particles while, Al2O3 is more effective than ZrO2. Addition of the ceramic particles enhanced the hydrophilicity properties of surface in wettability test and a contact angle of 43° was obtained for coating including Al2O3+ZrO2. The antibacterial properties of MAO coatings showed that S. aureus bacterium is more sensitive to the zirconia and alumina particle than S. typhimurium bacterium after 24 h of incubation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.