Abstract
Irradiation-assisted stress corrosion cracking (IASCC) is one of the critical concerns when stainless steel components have been in service in light water reactors for a long period. In-core IASCC growth tests have been carried out using the compact tension-type specimens of type 304 stainless steel that had been pre-irradiated up to a neutron fluence level around 1 × 1025 n/m2 under a pure water simulated boiling water reactor (BWR) coolant condition at the Japan Materials Testing Reactor (JMTR). In order to investigate the effect of synergy of neutron/gamma radiation and stress/water environment on SCC growth rate, we performed ex-core IASCC tests on irradiated specimens at several dissolved oxygen contents under the same electrochemical potential condition. In this paper, results of the in-core SCC growth tests are discussed and compared with the results obtained by ex-core tests from a viewpoint of the synergistic effects on IASCC. From results of in-core and ex-core tests using pre-irradiated specimens, the effect of synergy of neutron/gamma radiation and stress/water environment on SCC growth rate was considered to be small, because the in-core data under the same ECP condition were similar to the ex-core data under the DO = 32 ppm condition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.