Inclusion distribution in ingots was studied by dissection of a 16.8 t P12 ingot and a 5.0 t H13 ingot, with the analysis of T[O], original position statistic distribution analysis (OPA), metallographic microscope static analysis and small sample electrolysis. The results showed that the inclusions in ingots were uneven; a positive segregation area was found in the center and lower part of the ingot, while a negative segregation area was present in the central part of ingot top; inclusion segregation in a large size ingot was severer than that in a small one. A new concept, named inclusion segregation index, was put forward to quantify the segregation degree of inclusion. It was found that the segregation indexes drawn from T[O] analysis and OPA fit well, but they were different from those obtained by metallographic microscope static analysis and small sample electrolysis in the investigation of P12 ingot, which contained a higher sulfur content; while the segregation index drawn from T[O] analysis was close to that from metallographic microscope static analysis in the H13 ingot with a lower sulfur content.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.