Abstract
Abstract Based on XRD, SEM and EDS analyses, the phases in GH4151 alloy were identified. Differential scanning calorimetry (DSC) experiment and metallographic method were carried out to determine the incipient melting temperature (IMT) of the alloy. The result shows that the IMT of alloy is situated between 1150 and 1160 °C. Subsequently, the dissolution process of Laves phase was carried out, and the dissolution kinetic equations were obtained at different temperatures. And then based on the verification of experiments, the model was confirmed to be credible to predict the fraction of the Laves phase dissolution. Finally, the results of diffusion coefficients indicate that the diffusion of Nb element is a critical factor for homogenization process of GH4151 alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.