Abstract
High performance long-wavelength infrared nBn photodetectors based on InAs/InAs1−xSbx type-II superlattices on GaSb substrate have been demonstrated. The photodetector's 50% cut-off wavelength was ∼10 μm at 77 K. The photodetector with a 6 μm-thick absorption region exhibited a peak responsivity of 4.47 A/W at 7.9 μm, corresponding to a quantum efficiency of 54% at −90 mV bias voltage under front-side illumination and without any anti-reflection coating. With an R × A of 119 Ω·cm2 and a dark current density of 4.4 × 10−4 A/cm2 under −90 mV applied bias at 77 K, the photodetector exhibited a specific detectivity of 2.8 × 1011 cm. Hz/W.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.