This study aimed to assess the effect of length of the relocated cervical margin with casting post and core (CP), prefabricated fiber post and composite core (PFP), and polyethylene fiber-reinforced composite (PEFRC) on fracture resistance and marginal integrity. In this in vitro study, 70 sound human maxillary premolars were divided into seven groups according to the type of post and core system and length of the relocated cervical margin (n = 10): control (no preparation), PFP-3, PEFRC-3, CP-3 with 3 mm of cervical margin relocation (CMR), PFP-6, PEFRC-6, and CP-6 (with 6 mm of CMR). The samples were restored with zirconia crowns (except the control group). Epoxy resin replicas were fabricated before and after thermomechanical loading. Marginal integrity was assessed at the luting cement-core, core-tooth, and luting cement-enamel interfaces under a scanning electron microscope (SEM) (×200). Fracture resistance and failure mode were subsequently assessed. Data were analyzed by independent t-test, paired t-test, ANOVA, Tukey-Games Howell, Mann-Whitney, Kruskal-Wallis, Wilcoxon, Mann-Whitney with Bonferroni correction, and Fisher-Freeman-Halton tests (α = 0.05). The marginal integrity of the groups with 3 mm of CMR followed the following order: PEFRC > PFP > CP at all interfaces (P < 0.05). In 6-mm CMR groups, this order was CP < PFP = PEFRC at the luting cement-core and (CP < PEFRC) = PFP at the core-tooth interface. No significant difference was found in fracture resistance when comparing the 3-mm CMR groups with each other (P > 0.05). PFP-6 showed higher FR than CP-6 (P < 0.001). PEFRC-6 had no significant difference with PFP-6 and CP-6 (P > 0.05). In each post and core system, 3-mm CMR groups showed higher marginal integrity and fracture resistance (P < 0.05). Increasing the length of the relocated cervical margin decreased the marginal integrity and fracture resistance of all three systems of CP, PFP, and PEFRC.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.