The in vitro lifetime assessment of dental zirconia has been the focus of researchers. This work mainly studied the cyclic fatigue lifetime in saliva and aging lifetime of three commercial zirconia dental materials: two kinds of 3 mol%-yttria stabilized zirconia ST(super-translucence) and MT(medium-translucence), in which MT contains a small amount of alumina; a 5 mol%-yttria stabilized zirconia TT(tooth-translucency). ST and MT materials have higher initial mechanical strength (flexural strength) and initial crack propagation threshold than TT materials, thus they have longer cycle fatigue lifetime, but TT has best aging resistance(no aging) in existing aging procedures. MT has a higher initial mechanical strength and better aging resistance than ST samples due to the influence of alumina at grain boundary, but has lower strength reliability. Finally the service lifetime of the three materials was evaluated, and some guidance for their use is provided.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.