In Vitro Antibacterial and Cytotoxicity Assessments of an Orthodontic Bonding Agent Containing Benzalkonium Chloride

Abstract

To assess the antibacterial activity and cytotoxicity of an orthodontic bonding material containing an antibacterial agent. Superbond C&B (4-methacryloxyethyl trimellitate anhydride/methyl methacrylate-tri-n-butyl borane [4-META/MMA-TBB]) resin was mixed with benzalkonium chloride (BAC) to obtain final BAC concentrations of 0.25%, 0.75%, 1.25%, 1.75%, 2.5%, and 5.0% (wt/ wt). Antibacterial activity against Streptococcus mutans and Streptococcus sobrinus was evaluated by soaking the BAC-resin in distilled water at 37 degrees C for periods of 30, 90, and 180 days. Antibacterial activity of the BAC-resin was measured by the disk diffusion method, and the inhibition zone around each sample was measured and recorded. For evaluation of cytotoxicity, BAC-resin samples were put into cell culture inserts placed above human gingival cells and were incubated at 37 degrees C for 1, 3, and 6 days. Cytotoxicity was assessed with a tetrazolium bromide reduction assay. The antibacterial activity of BAC-incorporated resin samples decreased significantly after immersion in water for 180 days, regardless of BAC concentration. The antibacterial activity of nonimmersed resin containing 0.25% or 1.75% BAC was comparable with that of 5.0% BAC-resin immersed for 180 days. In cytotoxicity tests, most cells died when exposed to resins containing 1.75%, 2.5%, and 5% BAC. No difference was observed between resins containing 0.25% and 0.75% BAC at 1, 3, and 6 days of culture. The addition of BAC to 4-META/MMA-TBB resin confers an antibacterial effect even after immersion in water, and 4-META/MMA-TBB resin containing 0.25% to 0.75% BAC has no significant cytotoxic effect.