In Situ X-ray Absorption Spectroscopy of PtNi-Nanowire/Vulcan XC-72R under Oxygen Reduction Reaction in Alkaline Media.

Abstract

Studying the oxygen reduction reaction (ORR) in the alkaline electrolyte has proven to promote better catalytic responses and accessibility to commercialization. Ni-nanowires (NWs) were synthesized via the solvothermal method and modified with Pt using the spontaneous galvanic displacement method to obtain PtNi-NWs. Carbon Vulcan XC-72R (V) was used as the catalyst support, and they were doped with NH3 to obtain PtNi-NWs/V and PtNi-NWs/V–NH3. Their electrocatalytic response for the ORR was tested and PtNi-NWs/V provided the highest specific activity with logarithmic values of 0.707 and 1.01 (mA/cm2Pt) at 0.90 and 0.85 V versus reversible hydrogen electrode (RHE), respectively. PtNi-NWs showed the highest half-wave potential (E1/2 = 0.89 V) at 1600 rpm and 12 μgPt/cm2 in 0.1 M KOH at 25.00 ± 0.01 °C. Additionally, the catalysts followed a four-electron pathway according to the Koutecký–Levich analysis. Moreover, durability experiments demonstrated that the PtNi-NW/V performance loss was like that of commercial Pt/V along 10,000 cycles. Electrochemical ORR in situ X-ray absorption spectroscopy results showed that the Pt L3 edge white line in the PtNi-NW catalysts changed while the electrochemical potential was lowered to negatives values, from 1.0 to 0.3 V versus RHE. The Pt/O region in the in situ Fourier transforms remained the same as the potentials were applied, suggesting an alloy formation between Pt and Ni, and Pt/Pt contracted in the presence of Ni. These results provide a better understanding of PtNi-NWs in alkaline electrolytes, suggesting that they are active catalysts for ORR and can be tuned for fuel cell studies.