Abstract
In situ observation during hydrogen ion implantation was performed with a transmission electron microscope installed in an ion accelerator to investigate the growth process of Zr hydride in Zircaloy-4. To clarify the effect of radiation damage, some samples were irradiated with 4 MeV Ni3+ ions prior to hydrogen implantation. Growth processes of Zr hydrides accompanying the formation of dislocations were observed. The crystallographic relationship between the Zr matrix and Zr hydrides was identical with that found in previous studies: inter- and intragranular hydrides exhibiting a tendency to grow in the (112-0) direction. This growth can be attributed to a shear mechanism in which there are partial dislocations along basal planes. In specimens preirradiated with Ni ions, the growth rate of hydrides was suppressed, but the growth direction was not affected by radiation defects. It was also confirmed that the black spots induced by Ni3+ ion irradiation grew during hydrogen ion implantation, suggesting the f...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.