In situ Synthesis of Nickel Ferrite Nanoparticle/organic Hybrid

Abstract

A NiFe2O4 particle/organic hybrid was synthesized in situ from iron-organic and nickel organic compounds below 100 °C. A mixture of nickel (II) acetylacetonate (NA) and iron (III) 3-allylacetylacetonate (IAA) was hydrolyzed and polymerized yielding spinel oxide particle/oligomer hybrid. X-ray diffraction analysis revealed that the crystallinity of spinel particles was dependent upon the hydrolysis conditions of NA-IAA. Nanocrystalline nickel ferrite particles around 10 nm were uniformly dispersed in the organic matrix. The formation of nickel ferrite was confirmed by energy-dispersive x-ray and x-ray photoelectron spectroscopy. The saturation magnetization of hybrid increased with increasing water amount for hydrolysis. Nano-sized nickel ferrite particle/organic hybrid showed a BH curve with no remanence above 75 K. The magnetization versus H/T curves at 300, 200, and 75 K were superimposed on the same curve and satisfied the Langevin equation. The remanent magnetization and coercive field of the hybrid were 7.4 emu/g and 460 Oe, respectively, at 5 K.