Abstract

Kaolin-based graphitic carbon nitride (g-CNx) composite photocatalysts were synthesized from a urea precursor using a commercial kaolin. Structural characterization by X-ray diffraction and infrared spectroscopy (FTIR) verified the successful thermal polycondensation of g-CNx along the thermal dehydroxylation of kaolinite to metakaolin at 550 °C. The g-CNx content of the composites were estimated by thermogravimetry and CHN analysis, ranging from ca. 87 m/m% to ca. 2 m/m% of dry mass. The addition of kaolin during the composite synthesis was found to have a significant effect: the yield of in situ formed g-CNx drastically decreased (from ca. 4.9 m/m% to 3.8–0.1 m/m%) with increasing kaolin content. CHN and FTIR indicated the presence of nitrogen-rich g-CNx, having a specific surface area of 50 m2/g, which synergistically increased after composite synthesis to 67–82 m2/g. Estimated optical band gaps indicated the affinity to absorb in the visible light spectrum (λ < 413 nm). Photocatalytic activity upon both UV and artificial sunlight irradiation was observed by hydroxyl radical evolution, however, without the synergistic effect expected from the favorable porosity.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.