Abstract
An in situ temperature study of a variation in the degree of long-range order in stoichiometric titanium monoxide has been performed by the magnetic susceptibility method. The measurements have been performed on annealed and quenched titanium monoxide in the temperature range from 300 to 1200 K. It has been found that the degree of long-range order depends on the regime and temperature of annealing of the initial samples. The degree of long-range order in the process of measurement of the magnetic susceptibility varies from 0.21 to 1.00; the larger the degree of long-range order, the smaller the magnetic susceptibility. Furthermore, the long-range order parameter decreases with an increase in the temperature above 1200 K and vanishes sharply at the order-disorder transition temperature. According to the results of this work, the critical long-range order parameter is 0.21 and the temperature of the nonequilibrium disorder-order transition is about 1073 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.