Abstract
In situ X-ray photoelectron spectroscopy (XPS) was carried out over model Rh0.5Pd0.5 nanoparticles and Rh0.5Pd0.5 nanoparticles supported on CeO2 following exposure to oxygen at 573–823K, to hydrogen at 573K (activation of the catalyst), to a mixture of ethanol and water at 823K simulating ethanol steam reforming (ESR) conditions, and to hydrogen at 823K. The presence of the CeO2 support had a strong influence on the atomic rearrangement and on the oxidation state of Rh0.5Pd0.5 nanoparticles. CeO2 exerted a quenching effect on the metal nanoparticles and limited atomic rearrangement under the different atmospheres tested except for ESR, where a partial segregation of Rh toward the surface of the nanoparticles was observed. When supported on CeO2, Rh0.5Pd0.5 nanoparticles were significantly more oxidized due to metal-support interaction. By comparing these in situ XPS results with a previous operando near-ambient pressure XPS study conducted in a synchrotron facility at 0.05 mbar over the same samples, it is concluded that the information obtained for the unsupported Rh0.5Pd0.5 nanoparticles is similar in both cases, whereas Rh0.5Pd0.5 nanoparticles supported on CeO2 are clearly more oxidized and enriched in Pd in the volume sampled under operando ESR conditions compared to that obtained in the in situ experiments. The study of catalytic systems under operando conditions appears essential to identify the active species at work during ESR, as the restructuring driven by the reforming environment induces strong changes in their architecture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.