Abstract
We investigated dynamic interfacial phenomena at the slag-metal-refractory three-phase interface using a high temperature X-ray radiographic technique. Dynamic movement of the metal-slag line between Fe-11%Cr alloy and CaO-(SiO2 or Al2O3) slag was observed near the MgO-6%C refractory at 1823 K. We observed corresponding local corrosion of the refractory with CaO-SiO2 slag but it was negligible with CaO-Al2O3 slag. From a thermodynamic perspective, the Marangoni convection at the slag-metal-refractory interface is not the dominant factor determining the corrosion rate of the MgO-C refractory. Rather, it is the large solubility limit and the mass transfer in the slag phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.