Abstract
We used high-speed X-ray phase contrast imaging and infrared thermal imaging techniques to study the formation processes of adiabatic shear bands in aluminum 7075-T6 and 6061-T6 alloys. A modified compression Kolsky bar setup was used to apply the dynamic loading. A flat hat-shaped specimen design was adopted for generating the shear bands at the designated locations. Experimental results show that 7075-T6 exhibits less ductility and a narrower shear band than 6061-T6. Maximum temperatures of 720 K and 770 K were locally determined within the shear band zones for 7075-T6 and 6061-T6 respectively. This local high temperature zone and the resulting thermal instability were found to relate to the shear band formation in these aluminum alloys.