Abstract
NaCl induced atmospheric corrosion of ZnAl2Mg2 coated, electrogalvanised (EG) and hot dipped galvanised (HDG) steel was studied using in situ infrared reflection absorption spectroscopy, XRD and SEM. Initial corrosion leads to the formation of Mg/Al and Zn/Al layered double hydroxides (LDHs) on ZnAl2Mg2, due to the anodic dissolution of Zn–MgZn2 phases and cathodic oxygen reduction on Zn–Al–MgZn2, Al-phases and on zinc dendrites. In contrast to EG and HDG, were no ZnO and Zn5(OH)8Cl2⋅H2O detected. This is explained by the buffering effect of Mg and Al which inhibit the ZnO formation, reduce the cathodic reaction and corrosion rate on ZnAl2Mg2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.