Abstract
Mo, Si and B4C powders were used to fabricate 0.4MoB-0.1SiC-xMoSi2 composites by self-propagating high-temperature synthesis (SHS) and hot pressing (HP). The effects of MoSi2 content (x = 1, 0.75, 0.5 and 0.25) on phase composition, microstructure and properties of the composites were investigated. The results showed that the 0.4MoB-0.1SiC-xMoSi2 composite exhibited Vickers hardness of 10.7–15.2GPa, bending strength of 337–827MPa and fracture toughness of 4.9–7.0MPam1/2. The fracture toughness increased with the increasing volume fraction of MoB and SiC particles which were promoted by the toughening mechanisms, such as crack bridging, cracks deflection and crack branching. Moreover, the electrical resistivity showed an increasing trend with decreasing volume fraction of MoSi2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.