Abstract
The poor kinetic background with the four-electron transfer of the oxygen evolution reaction (OER) was eradicated using a nickel-based catalyst, which was identified as an alternative to noble-metal catalysts. Here, we report the simple in situ formation of an earth-abundant nickel oxyhydroxide (NiOOH) electrocatalyst for efficient OER in an alkaline medium. Electroless material preparation, namely, the direct modification of a gas diffusion layer (GDL) with a nickel salt, was studied, and the layered oxyhydroxide phase was found to influence the rate of the OER. Interestingly, complete OER studies were carried out without using any external binders; that is, the catalyst stabilized in an aqueous medium was directly exploited. The resulting in situ electrochemically tuned NiOOH@GDL shows a low overpotential of 294 mV to reach a current density of 20 mA cm-2, which is superior to most non-noble mono/bimetal oxides that have been studied as OER catalysts so far. The catalyst also shows better kinetics with a low Tafel slope value of 30 mV dec-1 for NiOOH@GDL-B. In addition, the stability of NiOOH@GDL-B was confirmed from a chronoamperometric study that was carried out for 30 h with no significant loss in activity. The electrochemical evolution of the materials was further scrutinized, and a high turnover frequency (TOF) of 1.1 × 10-4 s-1 was calculated at 300 mV. The consistency of the catalyst was proved with various post-OER characterization analyses, and it appears to be beneficial for developing an efficient electrocatalyst for OER in the near future.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.