Abstract
Graphite is considered to be the most auspicious anode candidate for potassium ion batteries. However, the inferior rate performances and cycling stability restrict its practical applications. Few studies have investigated the modulating the graphitization degree of graphitic materials. Herein, a nitrogen-doped carbon-coated carbon fiber composite with tunable graphitization (CNF@NC) through etching growth, in-situ oxidative polymerization, and subsequent carbonization process is reported. The prepared CNF@NC with abundant electrochemical active sites and a rapid K+/electron transfer pathway, can effectively shorten the K+ transfer distance and promote the rapid insertion/removal of K+. Amorphous domains and short-range curved graphite layers can provide ample mitigation spaces for K+ storage, alleviating the volume expansion of the highly graphitized CNF during repeated K+ insertion/de-intercalation. As expected, the CNF@NC-5 electrode presents a high initial coulombic efficiency (ICE) of 69.3%, an unprecedented reversible volumetric capacity of 510.2 mA h cm-3 at 0.1 A g-1 after 100 cycles with the mass-capacity of 294.9 mA h g-1. The K+ storage mechanism and reaction kinetic analysis are studied by combining in-situ analysis and first-principles calculation. It manifests that the K+ storage mechanism in CNF@NC-5 is an adsorption-insertion-insertion mechanism (i.e., the "1+2" model). The solid electrolyte interphase (SEI) film forming is also detected.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Advanced science (Weinheim, Baden-Wurttemberg, Germany)
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.