In situ atomic scale mechanisms of strain-induced twin boundary shear to high angle grain boundary in nanocrystalline Pt

Abstract

Twin boundary can both strengthen and soften nanocrystalline metals and has been an important path for improving the strength and ductility of nano materials. Here, using in-lab developed double-tilt tensile stage in the transmission electron microscope, the atomic scale twin boundary shearing process was in situ observed in a twin-structured nanocrystalline Pt. It was revealed that the twin boundary shear was resulted from partial dislocation emissions on the intersected {111} planes, which accommodate as large as 47% shear strain. It is uncovered that the partial dislocations nucleated and glided on the two intersecting {111} slip planes lead to a transition of the original <110> symmetric tilt ∑3/(111) coherent twin boundary into a <110> symmetric tilt ∑9/(114) high angle grain boundary. These results provide insight of twin boundary strengthening mechanisms for accommodating plasticity strains in nanocrystalline metals.