Abstract
In situ (Al 2O 3 + Al 3Zr) np/Al nanocomposites were successfully prepared by magneto-chemical melt reaction from Al–Zr(CO 3) 2 system. The solidification microstructure and mechanical properties are investigated. Results indicate that the size of majority in situ α-Al 2O 3 and Al 3Zr particles is about 80 nm, and the nano-sized particles are well distributed in the aluminum matrix. The ultimate tensile strength and yield strength of the nanocomposites are enhanced with the increasing of particulate volume fraction, and are markedly higher than that of (Al 2O 3 + Al 3Zr) p/Al composites synthesized under zero magnetic field. When the particulate volume fraction is 8%, The ultimate tensile strength σ uts, yield strength σ y, elongation δ and Vickers hardness of the (Al 2O 3 + Al 3Zr) np/Al nanocomposites are 326.7 MPa, 245.6 MPa, 18.6% and 125, respectively. The principal strengthening mechanism for (Al 2O 3 + Al 3Zr)np/Al nanocomposites may include Orowan strengthening, Grain-refined strengthening, Solid–solution strengthening and Dislocation strengthening.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call