Abstract
Solid-state hydrogen storage in metal hydrides offers highest volumetric energy storage densities and low working gas pressures at the same time. Recently developed metal hydride composites (MHC) consist of a hydride-forming metal alloy and a secondary phase, typically graphite, to realize form-stable composites and short loading and unloading times (<5 min). Hydride formation causes a volume expansion of the storage material. Thus, it is mandatory to characterize this behavior for the sake of system safety.This work focuses on the in-operando characterization of the volume expansion of MHC that could trigger mechanical stresses acting on the walls and internal assemblies of the storage container. MHC with different metal particle shapes (flakes and powder) were studied. In-operando neutron imaging of axially freely expanding MHC was applied to analyze the time-resolved and spatial concentration of hydrogen, reaction fronts and the evolution of volume expansion and stability of the MHC. Stress measurements revealed that stresses of up to 330% of the respective operating gas pressure occur for confined MHC. Both techniques combined deliver crucial information and implications for the design of safe (according to ISO 16111), efficient and dynamic metal hydride storage systems.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.