Abstract
Granulated raw materials with a particle size of 20–80 μm were prepared from a slurry of Na2CO3, CaCO3, and SiO2 (quartz) by the spray-dry method, and injected with carrier gas into a radio-frequency induction thermal plasma. Spherical particles 5–60 μm in size were obtained and analyzed. Thermo-gravimetric analysis and X-ray diffraction analysis showed that during the short flight of the order of milliseconds, all carbonates were decomposed and >95% quartz was reacted into a noncrystalline state. Glass transition was clearly observed by differential thermal analysis. Increase of the carrier gas from 3 to 6 L/min led to a decrease in the volatilization ratio of Na2O from 46% to 18% with a slight decrease of the reaction ratio of quartz in trade balance. Electron probe microanalysis showed that the volatilization could be attributed to an excess heating of small particles <30 μm, and suppression by the increase of carrier gas.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.