Abstract
The hydrogen embrittlement (HE) mechanism of QP980 steels laser welded joints with complex microstructures is unclear. The joint with hydrogen pre-charging fractured at the inter-critical heat affected zone (ICHAZ) in slow strain rate tensile test, and the relative loss of elongation amounted to 84.8 %. Hydrogen-induced microcracks mainly initiated inside martensite (∼ 60 %). Hydrogen-induced crack propagation paths of the joint were transgranular propagation of martensite and intergranular propagation of ferrite/martensite interface. The HE mechanism of the joint was the combination of the effects in hydrogen-enhanced localized plasticity (HELP) and hydrogen-enhanced decohesion (HEDE).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.