Improving wear and corrosion resistance of HVAF sprayed 316L stainless steel coating by adding TiB2 ceramic particles and CeO2

Abstract

316L stainless steel is used in a wide variety of corrosion-prone locations. However, its low hardness and poor tribological properties limit its application under heavy wear conditions. In this study, 316L Fe-based composite coatings co-doped with TB2 hard phases and rare-earth CeO2 exhibited excellent wear and corrosion resistance. Firstly, 316L-TiB2 cermet powder and (316L-TiB2)/CeO2 composite powder with high sphericity and density were prepared by high energy ball milling (HEBM), spraying drying granulation (SD), plasma spheroidization (PS) process. Then, 316L coatings, 316L-TiB2 and (316L-TiB2)/CeO2 cermet coatings were deposited by high velocity air fuel (HVAF) spraying. Finally, the effects of TiB2 and CeO2 additions on the microstructure, wear and corrosion behavior of the coatings were investigated. The results showed that TiB2 hard particles and CeO2 were uniformly distributed in the HVAF sprayed 316L-TiB2 and (316L-TiB2)/CeO2 coatings. The wear resistance of the coating prepared by 316L Fe-based composite powder with TiB2 and CeO2 is significantly improved. The hardness of the (316L-TiB2)/CeO2 composite coating was increased from 269 Hv0.3 to 826 Hv0.3 for the pure 316L coating, while the volumetric wear rate was only 3.6 % of that of the pure 316L coating (110 × 10−5 down to 4 × 10−5 mm3/N). Electrochemical tests show that the corrosion resistance of the coating decreases with the addition of TiB2 alone, but it can be improved by doping CeO2. The 316L Fe-based coating prepared by adding TiB2 and CeO2 can significantly improve the wear resistance of the coating, while the corrosion resistance decreases only slightly.