Abstract
To obtain high-rebound resilience of crosslinking low-density polyethylene (LDPE) foam and decrease the foam density at the same content of foaming agent, the melt viscoelasticity of LDPE with different compositions (ethylene vinyl acetate [EVA], polyethylene-octene elastomer, and crosslinking agent) was investigated by dynamic rheology test. Then, LDPE/EVA/(polyethylene-octene elastomer) foams with different composition ratios were produced by a continuous foaming process and investigated by the rebound resilience test. The results show that the melt viscoelasticity behavior of LDPE and its blends in the molten state possessed more melt elasticity behavior after the crosslinking was introduced. Meanwhile, the rebound resilience of LDPE foam was increased 54% at the lower foam density (0.031 g/cm3). It could meet the requirements of sports mats for high-rebound resilience (>50%) and decrease the material cost when EVA was introduced into the foaming system. J. VINYL ADDIT. TECHNOL., 22:61–71, 2016. © 2014 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.