Abstract
This paper deals with the microstructure and thermal shock behavior of laser remelting of yttria-stabilized zirconia (YSZ) thermal barrier coatings (TBCs) deposited by plasma spraying. The microstructures of the coatings were analyzed by scanning electron microscopy (SEM). It was found that the as-sprayed ceramic coating had laminated structure with high porosity. However, the coating exhibited a dense lamellar-like layer with segment cracks on the remained plasma-sprayed porous layer. Thermal shock experiments for the two kinds of TBCs were performed by water quenching method. Testing result showed that the laser-remelted TBC had better thermal shock resistance than the as-sprayed one. The damage mode of the as-sprayed TBC was great-size whole spalling. In contract, the failure mechanism of the laser-remelted one was mainly local pelling. Segmented cracks of the top ceramic coatings caused by laser remelting improved the stress accommodation and were mainly attributed to the enhancement for thermal shock life of TBC.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.