Improving thermal shock and oxidation resistance of Cr3C2/WC-NiCr cermet coating by embedding large NiCrAlY superalloy particles

Abstract

Cr3C2/WC-based cermet coating is widely used on the surface of mechanical equipment to strengthen its wear and corrosion resistance. Improving the high-temperature performance of cermet coating is the key to its industrial application. In this study, a novel type of bimodal microstructure cermet coating with the design of functional sites was fabricated via high-velocity air fuel (HVAF) spray technology. The toughness NiCrAlY superalloy particles are introduced into the traditional Cr3C2/WC-NiCr cermet structure to construct the thermal stress release site, which significantly improved the thermal shock resistance and thermal oxidation properties of the coating. The addition of NiCrAlY superalloy particle reduces the porosity of Cr3C2/WC-NiCr coating to 0.29 % and creates high-quality interface bonding and surface passivation layer. The newly structured cermet coating exhibits outstanding high-temperature performance. In a 1000 °C oxidation environment, the new coating remained intact after 120 h of exposure, while the traditional Cr3C2/WC-NiCr cermet coating exfoliated completely after 48 h of exposure. Further, in the thermal shock condition at 1000 °C, the lifetime of the new coating is 50 times greater than that of the traditional cermet coating, displaying excellent ability to relieve thermal stress. Additionally, the new coating shows good wear resistance and stability during high-temperature thermal exposure. After thermal exposure for 24 h and 72 h, the wear rates of the coating are 5.28 and 5.83 × 10−5 mm3 N−1 m−1, respectively, which is slightly lower than that of the as-sprayed coating. This study provides guidance for the improvement of high temperature resistance of thermally sprayed Cr3C2/WC-based cermet coatings.