Abstract
The tensile strength of a CNT yarn was improved through simple one-step double [2+1] cycloaddition reactions that crosslinked the constituent CNTs using a polyethylene glycol (PEG)-diazide crosslinker. The FT-IR spectrum confirmed that the azide groups in the PEG-diazide were converted into aziridine rings, indicating that the cycloaddition reaction was successful. The generation of crosslinked CNTs was also supported by the observation of N1s peak in the XPS spectrum and the increased thermal stability of the material, as observed by TGA. The tensile strength of the CNT yarn was increased from 0.2GPa to 1.4GPa after the crosslinking reaction when twisted at 4000 twists/ meter. The appropriate selection of the crosslinker may further optimize the CNT yarn crosslinking reaction. The simplicity of this one-step crosslinking reaction provides an economical approach to the mass production of high-strength CNT yarns.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.