Abstract Poly(lactic acid) (PLA) biocomposites are usually plasticized to overcome the problem of poor ductility, which decreases the valuable tensile strength. In this study, novel nanofibrillated cellulose (NFC) was extracted to enhance the acetyl tributyl citrate (ATBC) plasticized PLA biocomposites. Interestingly, NFC not only exhibited an excellent strengthening effect but also showed a further toughening effect in the biocomposites. When 4 wt% NFC was added, the tensile strength, elongation at break, and impact strength of the biocomposites with 15 wt% ATBC and 20 wt% ATBC reached 52.6 MPa, 28.4%, 34.9 J/m and 35.8 MPa, 300.1%, 40 J/m, respectively. This is at least 1.1 folds higher in strength and 2.3 folds higher in impact toughness than the biocomposites without NFC. Glass transition and melting temperature slightly increased with NFC addition. More importantly, the mechanism of the strengthening and toughening effect was definitely elucidated, and the comprehensive performance of the application was evaluated. The findings of the study provide significant guidance for PLA application, such as in food packaging, medical engineering materials, and household products.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.