Abstract
AbstractRecently, surface crack nondamaging technology has been developed to render harmless surface cracks that can reduce the fatigue limit of metals by 20–60%. This is due to the effects of compressive residual stress induced by shot peening. To improve the reliability of high‐strength steel equipment designed against fatigue limit using surface crack nondamaging technology, the following characteristics were determined: (1) the effects of surface crack aspect ratio on maximum harmless crack depth (ahlm) at high‐strength steel for three residual stress distributions; (2) the relationship between the maximum allowable crack depth (acrN) and ahlm assuming the value of safety factor; (3) the relationship between minimum detectable crack depth via nondestructive inspection (aNDI) and ahlm, assuming that nondestructive inspection could detect the crack with sufficient probability; and (4) the relationships between ahlm, aNDI, and acrN.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.