Abstract

Abstract Recently, the use of wearable smart devices has significantly increased; however, sweat can corrode the outer-layer films, thereby decreasing their transmittance, conductivity, and overall functionality. In this study, fluorine-doped tin oxide (FTO) films for wearable smart devices were prepared via magnetron sputtering. The effects and mechanism of O2 gas flow in plasma on the properties of the fabricated films were investigated. Minor changes were observed in the film morphologies, with the preferred orientations shifting from polar (101) to nonpolar (110) and standard positions. As the O2 flow rate increased from 0 to 2 sccm, the transmittance of the film within the visible spectrum increased from 83% to 89%, with sheet resistance values in the order of 102–106 Ω·sq–1. Following immersion in an acidic sweat solution, the film without O2 peeled off, whereas several corrosion pits were observed in the films with 1 or 2 sccm O2. Conversely, following immersion in an alkaline sweat solution, several pits were observed in the films without O2, while the other films exhibited excellent corrosion resistance. The transmittance of the films immersed in different solutions did not significantly differ. Notably, the sheet resistances of the films treated with 1 sccm O2 met the industrial requirement of 3000 Ω. Moreover, the coexistence of polar and nonpolar planes provided transparency and conductive stability to the FTO films treated with 1 sccm O2. Our study aimed to not only enhance the transmittance and sweat-corrosion resistance but maintain the conductivity of the outer screen layer of a wearable smart electronic device.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.