Abstract
Glass-forming ability and crystallization behavior of various compositions in the CaO–Al 2O 3–TiO 2–P 2O 5 system were investigated, using differential thermal analyzer (DTA), X-ray diffractometry (XRD) and scanning electron microscopy (SEM) methods. According to our experiments, the precipitated crystalline phases were altered and the glass-forming and crystallization behaviors improved simultaneously, by addition of Al 2O 3 to the system. In the most promising composition, calcium pyrophosphate (Ca 2P 2O 7) and calcium titanium phosphate (CaTi 4(PO 4) 6) were formed during an ordinary short time heat treatment around the first DTA crystallization peak temperature of it. However, long-term heat treatment led to crystallization of calcium pyrophosphate (Ca 2P 2O 7) and titanium pyrophosphate (TiP 2O 7) phases. Chemical leaching of the optimum resulted glass-ceramic with HCl, caused that calcium pyrophosphate was selectively dissolved out and a porous skeleton of titanium pyrophosphate remained. Porous structure of final products seems to be conceivable for applications as filters, membranes, catalyst supports, etc.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.