Abstract
Laser surface melting (LSM) pretreatment and micro-arc oxidation (MAO) were performed to the AZ91D magnesium alloy to improve the corrosion resistance. The microstructure, surface morphologies, phase constituents and electrochemical corrosion behavior were investigated by optical microscope (OM), scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD) and electrochemical impedance spectroscopy (EIS) measurements respectively. The results showed that the AZ91D alloy obtained a continuous and uniform laser-melted layer with a thickness of 1 mm and refined microstructure. The MAO coating on laser-melted AZ91D magnesium alloy had refined micro-pores with uniform size than that on the original magnesium substrate without laser melting pretreatment, and correspondingly, the lower corrosion current density and larger MAO coating electrochemical impedance value were found on the AZ91D magnesium alloy with LSM and MAO treatment. It implies that the LSM-MAO coating had more effect on improving the corrosion resistance compared with the singular MAO coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.